Product Description
LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and injection molding applications. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams. LDPE is particularly suitable for applications that require excellent processability and optical proterties.
|
Max conductor temperature:
|
90°C
|
|
Tensile Strength:
|
≥ 13.5Mpa
|
|
Elongation at Break:
|
≥ 350%
|
|
Brittleness temperature:
|
≤ -76°C
|
|
Ageing Properties (Test temperature 135°C, 168h)
Max Variation of tensile strength:
Max Variation of elongation at break:
|
± 20%
± 20%
|
|
Hot Set Test (200°C, 15min, 0.2MPa)
Max elongation under load:
Max permanent elongation after cooling:
|
≤ 100%
≤ 5%
|
|
Dielectric constant (20°C, 50HZ):
|
≤ 2.35
|
|
Dissipation factor (20°C, 50HZ):
|
≤1.0x10(-3)
|
|
Volume Resistance (20°C):
|
≥ 1.0x10(16)Ω.cm
|
|
Dielectric strength:
|
≥ 25Mv/m
|